Oloa
57% Translucency 3D Plus Multilayer Dental Zirconia Poloka False Dental Zirconia Discs
Fa'amatalaga Puupuu:
57% Translucency 3D Plus Multilayer Dental Zirconia Poloka False Dental Zirconia Discs
Nifo 1500℃ zirconium poloka ma 49 zirconium poloka ma ce nifo zirconia avanoa fa'aoga i poloka zirconia sese
Folasaga o le YUCERA's 3D Plus Multilayer dental zirconia:
3D plus multilayer zirconia poloka ose nifo zirconia (Y-TZP ZrO2) mo toe faʻaleleia e sili ona susulu, monolithic.3D plus multilayer zirconia poloka ofo atu ma le 700-1050MPa se malosi fa'afefete maualuga maualuga fa'atasi ma le translucency maualuga.O mea vaivai a'o le'i sintering e fa'amautinoa ai se fa'agasologa o le gaosiga e aunoa ma se taumafaiga.E mafai ona fa'a'ofuina uma sima i faiga masani uma (silasila i le tau CET).
Vaega o le 3D Plus Multilayer dental zirconia/ceramic block/blank/discs:
1. Sintered Density of zirconia disc 6.07 ± 0.03g/cm3
2. Fa'alelei tulaga ese - maualuga translucent ma maualuga malosi.
3. Translucency o zirconia tisiketi 57-43%
4. Filifiliga lanu tele - 19 lanu (Blench, A1-D4).
5. Fa'apa'u Malosi o le zirconia disc700-1050 MPa
6. Malosi o zirconia tisiki 1200HV
7. Fa'ailoga lautele - mai le toe fa'afo'iina o nifo e tasi i le alalaupapa fa'aopoopo.
8. Vita 16 lanu o A1-D4 ma Blench OM1 / 2/3 lanu
9. poloka zirconia nifo lanu lava ia
10. CAD CAM faiga numera
11. High translucent zirconium oxide mo le matagofie atoatoa
Fa'atonuga Filifiliga
1. Monolithic gaioiga po'o se vaega sima vetata'i
2. E mafai ona fa'aoga le pulumu po'o le fufui
Fa'ailoga
Toe fa'afo'isia nifo tasi (i luma ma tua)
3-iunite alalaupapa (tua ma tua)
Alalaupapa tele-iunite ma NexxZr + paepae (tua ma tua)
afifiina
Tisiki Tasi
YUCERA fa'asologa uma
| Ituaiga | Code | Translucence | Malosi punou | Malosi | Lanu | Tele |
| Poloka zirconia paʻepaʻe | HT | 40% | ≧1200Mpa(Av.) | 1200HV | Pa'epa'e (vai lanu ma le vita 16 lanu ma le 26 paolo | Tatala faiga& Zirkon zahn faiga & Amann Girrbach System |
| ST | 43% | ≧1200Mpa(Av.) | 1200HV | |||
| Poloka zirconia fa'ailoga | ST-lanu | 43% | ≧1100Mpa(Av.) | 1200HV | Vita 16 lanu ma BL1, BL2, BL3 | |
| Poloka zirconia fa'apipi'i fa'atele | SHT-ML | 46% | ≧900Mpa(Av.) | 1200HV | ||
| UT-ML | 49% | ≧600Mpa(Av.) | 1200HV | |||
| 3D Plus-ML | 43%-57% | ≧700Mpa(Av.)–1050Mpa(Av.) | 1200HV |
E talafeagai mo lalo faiga
| Tatala Cadcam System | Zironzahn System | Amann Girrbach |
| 98x10mm | 95x10mm | / |
| 98x12mm | 95x12mm | AGx12mm |
| 98x14mm | 95x14mm | AGx14mm |
| 98x16mm | 95x16mm | AGx16mm |
| 98x18mm | 95x18mm | AGx18mm |
| 98x20mm | 95x20mm | AGx20mm |
| 98x22mm | 95x22mm | AGx22mm |
| 98x25mm | 95x25mm | AGx25mm |
| SHT Multilayer/UT Multilayer /3D Multilayer Sintering Curve | ||||
| Laasaga fa'amau | Amata le vevela(℃) | Fa'ai'uga vevela(℃) | Taimi(Min) | Fua (℃/Min) |
| Laasaga 1 | 20 | 900 | 90 | 9.7 |
| Laasaga 2 | 900 | 900 | 30 | 0 |
| Laasaga 3 | 900 | 1500 | 180 | 3.3 |
| Laasaga 4 | 1500 | 1500 | 120 | 0 |
| Laasaga 5 | 1500 | 800 | 60 | -11.6 |
| Laasaga 6 | 800 | mālū fa'anatura 20 | 120 | -6.5 |