57% translucidité 3D plis multikouch dantè zirkonya blòk fo dantè zirkonya disk
Deskripsyon kout:
57% translucidité 3D plis multikouch dantè zirkonya blòk fo dantè zirkonya disk
Dantè 1500 ℃ blòk zirkonyòm ak 49 blòk zirkonyòm ak ce dantè zirkonya vid ki itilize nan fo blòk zirkonya
Entwodiksyon nan zirkonya dantè 3D Plus Multilayer YUCERA a:
3D plis multikouch zirkonya blockis yon zirkonya dantè (Y-TZP ZrO2) pou trè translusid, restorasyon monolitik.3D plis multikouch blòk zirkonya ofri ak 700-1050MPa yon eksepsyonèl gwo fòs flexural konbine avèk translusid segondè.Materyèl la mou anvan SINTERING asire yon pwosesis manifakti san efò.Placage tout-seramik posib ak sistèm komen tout-seramik yo (gade valè CET).
Karakteristik 3D Plus Multilayer zirkonya dantè / blòk seramik / vid / disk:
1. Sintered Dansite zirkonya disk 6.07 ± 0.03g/cm3
2. Estetik eksepsyonèl - segondè translusid ak gwo fòs.
3. Translusid nan zirkonya disk 57-43%
4. Gwo seleksyon koulè - 19 koulè (Blench, A1-D4).
5. koube fòs zirconia disc700-1050 MPa
6. Dite nan zirkonya disk 1200HV
7. pakèt endikasyon - soti nan yon sèl-dan restorasyon nan milti-inite pon.
8. Vita 16 koulè nan A1-D4 ak Blench OM1/2/3 koulè
9. Blòk zirkonya dantè ki gen koulè pal
10. CAD CAM sistèm dijital
11. Segondè translusid zirkonyòm oksid pou estetik pafè
Opsyon pwosesis
1. Monolitik pwosesis oswa pasyèl seramik veneering
2. Si ou vle bwòs oswa plonje enfiltrasyon posib
Endikasyon
Retablisman yon sèl dan (anteryè ak dèyè)
3-inite pon (anteryè ak dèyè)
Multi-inite pon ak NexxZr + blan (anterior ak dèyè)
Anbalaj
Single disk
YUCERA tout seri
| Kalite | Kòd | Translusid | Fòs koube | Dite | Koulè | Gwosè |
| Blòk zirkonya blan | HT | 40% | ≧1200Mpa (Av.) | 1200HV | Blan (likid koloran ak Vita 16 tout koulè ak 26 tout koulè | Louvri sistèm & Zirkon zahn sistèm & Amann Girrbach Sistèm |
| ST | 43% | ≧1200Mpa (Av.) | 1200HV | |||
| Blòk zirkonya preshaded | ST-Koulè | 43% | ≧1100Mpa (Av.) | 1200HV | Vita 16 tout koulè ak BL1, BL2, BL3 | |
| Multikouch preshaded blòk zirkonya | SHT-ML | 46% | ≧900Mpa (Av.) | 1200HV | ||
| UT-ML | 49% | ≧600Mpa (Av.) | 1200HV | |||
| 3D Plus-ML | 43% -57% | ≧700Mpa (Av.)–1050Mpa (Av.) | 1200HV |
Apwopriye pou sistèm anba a
| Louvri sistèm Cadcam | Sistèm Zironzahn | Amann Girrbach |
| 98x10mm | 95x10mm | / |
| 98x12mm | 95x12mm | AGx12mm |
| 98x14mm | 95x14mm | AGx14mm |
| 98x16mm | 95x16mm | AGx16mm |
| 98x18mm | 95x18mm | AGx18mm |
| 98x20mm | 95x20mm | AGx20mm |
| 98x22mm | 95x22mm | AGx22mm |
| 98x25mm | 95x25mm | AGx25mm |
| SHT Multileyer / UT Multilayer / 3D Multilayer Sintering Curve | ||||
| Sintering etap | Kòmanse Tanperati (℃) | Tanperati fen (℃) | Tan (Min) | To (℃/Min) |
| Etap 1 | 20 | 900 | 90 | 9.7 |
| Etap 2 | 900 | 900 | 30 | 0 |
| Etap 3 | 900 | 1500 | 180 | 3.3 |
| Etap 4 | 1500 | 1500 | 120 | 0 |
| Etap 5 | 1500 | 800 | 60 | -11.6 |
| Etap 6 | 800 | refwadisman natirèl 20 | 120 | -6.5 |