57% Translucency 3D Plus Multilayer Dental Zirconia Toshe Ƙarya Fayafan hakori Zirconia
Takaitaccen Bayani:
57% Translucency 3D Plus Multilayer Dental Zirconia Toshe Ƙarya Fayafan hakori Zirconia
Dental 1500 ℃ tubalan zirconium da 49 zirconium tubalan da ce hakori zirconia blank amfani da karya zirconia tubalan.
Gabatarwar YUCERA's 3D Plus Multilayer hakori zirconia:
3D tare da multilayer zirconia blockis a hakori zirconia (Y-TZP ZrO2) don sosai m, monolithic gyare-gyare.3D da multilayer zirconia block yana ba da 700-1050MPa babban ƙarfin sassauƙa mai ƙarfi haɗe tare da babban haske.Abu mai laushi kafin sintering yana tabbatar da aiwatar da ƙirar ƙira.Duk wani yumbu mai yumbu mai yuwuwa tare da tsarin gama-gari na yumbu (duba ƙimar CET).
Siffofin 3D Plus Multilayer hakori zirconia/ceramics block/blank/ discs:
1. Sintered Density of zirconia disc 6.07 ± 0.03g/cm3
2. Fitattun kayan ado - high translucent da high ƙarfi.
3. Fassarar diski na zirconia 57-43%
4. Zaɓin launi mai yawa - 19 launuka (Blench, A1-D4).
5. Lankwasawa Ƙarfin Zirconia disc700-1050 MPa
6. Taurin faifan zirconia 1200HV
7. Faɗin alamomi - daga maidowa haƙori guda ɗaya zuwa gada mai raka'a da yawa.
8. Vita 16 launi na A1-D4 da Blench OM1/2/3 launi
9. Tubalan zirconia masu launin kai
10. CAD CAM tsarin dijital
11. High translucent zirconium oxide ga cikakken aesthetics
Zaɓuɓɓukan sarrafawa
1. sarrafa monolithic ko ɓangaren yumbu veban tsoro
2. Goga na zaɓi ko tsoma kutse mai yiwuwa
Alamomi
Maido da hakora guda ɗaya (gaba da baya)
Gada guda 3 (na gaba da na baya)
Gada mai raka'a da yawa tare da NexxZr + fari (na gaba da na baya)
Marufi
Disc guda ɗaya
YUCERA duk jerin
| Nau'in | Lambar | Fassara | Karfin Lankwasawa | Tauri | Launi | Girman |
| Farin toshe zirconia | HT | 40% | ≧1200Mpa (Av.) | 1200HV | Fari (ruwa mai launi tare da vita 16 tabarau da 26 inuwa | Bude tsarin&Tsarin Zirkon zahn & Tsarin Amann Girrbach |
| ST | 43% | ≧1200Mpa (Av.) | 1200HV | |||
| Tushen zirconia da aka rigaya | ST-Launi | 43% | ≧1100Mpa (Av.) | 1200HV | Vita 16 tabarau da BL1, BL2, BL3 | |
| Multilayer preshaded zirconia block | SHT-ML | 46% | ≧900Mpa (Av.) | 1200HV | ||
| UT-ML | 49% | ≧600Mpa (Av.) | 1200HV | |||
| 3D Plus-ML | 43% -57% | ≧700Mpa(Av.)–1050Mpa(Av.) | 1200HV |
Ya dace da tsarin ƙasa
| Bude Tsarin Cadcam | Tsarin Zironzahn | Amann Girrbach |
| 98x10m ku | 95x10mm | / |
| 98x12m ku | 95x12mm | AGx12mm |
| 98x14m ku | 95x14mm | AGx14mm |
| 98x16 ku | 95x16 ku | AGx16mm |
| 98x18m ku | 95x18mm | AGx18mm |
| 98x20 ku | 95x20mm | AGx20mm |
| 98x22mm | 95x22mm | AGx22mm |
| 98x25 ku | 95x25mm | AGx25mm |
| SHT Multileyer/UT Multilayer / 3D Multilayer Sintering Curve | ||||
| Sintering mataki | Fara Zazzabi(℃) | Ƙarshen Zazzabi(℃) | Lokaci (min) | Ƙimar (℃/min) |
| Mataki na 1 | 20 | 900 | 90 | 9.7 |
| Mataki na 2 | 900 | 900 | 30 | 0 |
| Mataki na 3 | 900 | 1500 | 180 | 3.3 |
| Mataki na 4 | 1500 | 1500 | 120 | 0 |
| Mataki na 5 | 1500 | 800 | 60 | -11.6 |
| Mataki na 6 | 800 | sanyaya dabi'a 20 | 120 | -6.5 |