♠ 6 layers Multilayer color
♠ From 43% to 57% gradient for transparency
♠ Strength shows gradient from 10500 Mpa to 700 Mpa
♠ Suitable for anterior, crown, 7 unit bridges and all restoration
Crown /Inlay /Onlay /Implant /Anterior/Posterior/Veneer
Sintered Density | 6.07 ± 0.03g/cm3 |
Hardness | 1200HV |
Sintering Temperature | Recommend 1500℃ |
Bending Strength | 1050Mpa-700Mpa |
Translucency | 43%-57% |
Safety: No irritation,No corrosion,Good bio-compatibility
Beauty: Natural teeth color can be reproduced
Comfortability: Low thermal conductivity,hot and cold changes do not stimulte the pulp
Durability: Over 1600MPa perturbed strength, durable and useful
As the leading manufacturer of dental zirconia block in china, Yucera zirconia block includes white zirconi block(HT, ST, UT), pre-shaded zirconia block (ST-color,) and multilayer preshaded zirconia block(SHT, UTMultilayer, 3D Plus Multilayer).
Type | Code | Translucency | Bending Strength | Hardness | Color | size |
white zirconia block | HT | 40% | ≥1200Mpa(Av.) | 1200HV | white (coloring liquid with vita 16 shades and 26 shades | Open system & Zirkon zahn system (D98*10-25mm & D95*10-25mm |
white zirconia block | ST | 43% | ≥1200Mpa(Av.) | 1200HV | same as above | same as above |
Shade zirconia block | ST-color | 43% | ≥1100Mpa(Av.) | 1200HV | Vita 16 shades and BL1, BL2, BL3, BL4 | same as above |
Multi zirconia block | SHT-ML | 46% | ≥900Mpa(Av.) | 1200HV | same as above | same as above |
Multi zirconia block | UT-ML | 49% | ≥600Mpa(Av.) | 1200HV | same as above | same as above |
Multi zirconia block | 3D Plus-ML | 43%-57% | ≥10500Mpa(Av.)-≥700Mpa(Av.) | 1200HV | same as above | same as above |