98x10mm White 1200MPA Dental Zirconia Blank For Lab – Yurucheng

YUCERA Dental Materials And Equipment Manufacturer Economical Dental Zirconia Blanks For Dental Laboratory

To achieve expected quality, the sintering curves for dental zirconia blanks must be followed.

Note: please employ high-temperature furnace specially designed for denture manufacturing. It is good for ceramics sintering to prolong heating up time and cooling time properly.

1. Sintering preparation: Make sure there is enough sintering space to avoid deformation. After dyeing, the restoration must be dried. Do not heat up too quickly for it might result in cracks. Make sure the dust-proof cover is put on the crucible to keep impurity away from restorations

2. After sintering: Following the instruction to lower temperature and take out restorations. Do not reduce furnace temperature too quickly to avoid cracks.

3.The highest temperature: the highest temperature will affect the translucency and dyeing results. Make sure the accurate temperature of every step. Sinter and preserve heat according to the instruction.

Yucera zirconia block has high strength, excellent permeability and color aesthetic repair effect that suitable for CAD/CAM system and manual system.

Dental Zirconia Blanks Features

Safety:No irritation,No corrosion,Good bio-compatibility

Beauty:Natural teeth color can be reproduced

Comfortability:Low thermal conductivity,hot and cold changes do not stimulte the pulp

Durability:Over 1600MPa perturbed strength, durable and useful

HT Zirconia Block

*High translucent

*Brilliant bending strength and economic block

*Suitable for coping and framework

Indications of dental zirconia blanks

Coping, Inlay, Onlay, Bridge, Crown

Physical Characteristics of dental zirconia blanks